Products

Hot rolled coil

Qual UNI / Norma Re Min Re Max Rm Min Rm Max A80% NOTE
Cold forming steel . Trasversal direction
EN 10111
DD11 170 360 – 440 23 As per materials with thikness ≥2 – Re max 340 – A80% min 24 – If thikness ≥3 A(L0=5,56 √S0)% min 28
DD12 170 340 – 420 25
DD13 170 330 – 400 28
DD14 170 310 – 380 31
Structural steel (* weathering steel), Trasversal test
EN 10025
S235JR 235 – 360 510 15 Note1: As per thikness ≤ 16 mm – Note2:as per longitudinal tes A80% min +2%. Note 3 A80% trasversalmin for thikness if ≤1 = 15% – se ≤1,5 = 16% – if ≤2 = 17% – if ≤2,5 = 18% – if < 3 = 19%. Note 3: sif thikness ≥ 3 A(L0=5,56 √S0)% min 24- note 4: as for sheets , and strip with width < 600 longitudinal test
S235J0 235 – 360 510 15
S235J2 235 – 360 510 15
S275JR 275 – 430 580 15 Note 1: Re as per thikness ≤ 16 mm – Note2:as per longitudinal testA80% min +2%. Note3 A80% trasversal min for thikness: if ≤1 = 13% – if ≤1,5 = 14% – if ≤2 = 15% -if ≤2,5 = 16% – if< 3 = 17%. Note3: if thikness ≥ 3 A(L0=5,56 √S0)% min 21- note4: as for sheets , and strisi with width < 600 longitudinal test – Nota5: as per thikness ≥3 Rm min and max – 20
S275J0 275 – 430 580 15
S355JR 355 – 510 680 12 Nota1: Re as per thikness ≤ 16 mm – Note2:as per longitudinal test A80% min +2%. Nota3 A80% trasversal min for thikness: if ≤1 = 12% – if ≤1,5 = 13% – if≤2 = 14% – if ≤2,5 = 15% – if < 3 = 16%. Note3: if thikness ≥ 3 A(L0=5,56 √S0)% min 20- note4: as for sheets , and strips with width < 600 longitudinal test – Note5: as per thikness ≥3 Rm min-40 and rm max – 50
S355J0 355 – 510 680 12
S355J2 355 – 510 680 12
*S355J0W 355 – 510 680 14 Nota1: Re as per thikness ≤ 16 mm – Nota2:as per longitudinal test A80% min +2%. Note3 A80% trasversal min for thikness: if >1,5 and ≤2 = 14% – if >2 and ≤2,5 = 15% – if <2,5 and <3 = 16%. Note3: if thikness≥ 3 A(L0=5,56 √S0)% min 20 – note4: as for sheets , and strips with width < 600 longitudinal test – Note5: It’s enought presence of of those elements: Al,Nb,V,Ti
S450JO 450 – 550 720 17 Nota1: As per thikness ≤ 16 mm – Note2: Rm for thikness ≥3 – Note3: A80% not declared A(L0=5,56 √S0)% for thikness ≥3<40 mm
S185 185 – 310 540 8 Nota1: Re per spessori ≤ 16 mm – Nota2:per test longitudinale A80% min +2%. Nota3 A80% trasversale min per spessore: se ≤1 = 8% – se ≤1,5 = 9% – se ≤2 = 10% – se ≤2,5 = 11% – se < 3 = 12%. Nota3: se spessore ≥ 3 A(L0=5,56 √S0)% min 16- nota4: per fogli , e nastri con larghezza < 600 test longitudinale – Nota5: per spessori ≥3 Rm min-20 e rm max – 30
High resistance Microalloy steel, longitudinal test
EN 10149
S315MC 315 – 390 510 20 1- If thikness < 3 A80% if ≥3 A5,56 √S0%
S355MC 355 – 430 550 19
S420MC 420 – 480 620 16
S460MC 460 – 520 670 14
S500MC 500 – 550 700 12
S550MC 550 – 600 760 12
S600MC 600 – 650 820 11
S650MC 650 – 700 880 10
S700MC 700 – 750 950 10
Surface treatments available Hot rolled, pickled, pickled and oiled

Cold rolled coil

Qual UNI / Norma Re Min Re Max Rm Min Rm Max A80% NOTE
Deep drawing and cold banding steel . Trasversal test
EN 10130
DC01 140 280 270 410 28 Thikness ≤ 0,7 and > 0,5 – Re max + 20 Mpa and A80% min – 2%. — Thikness ≤ 0,5 Re max + 40 Mpa and A80% min – 4%.
DC03 140 240 270 370 34
DC04 140 210 270 350 38
DC05 140 180 270 330 40
DC06 120 170 270 330 41
DC07 100 150 250 310 44
Micro Alloy steel. Trasversal steel
EN 10268
HC260LA 260 330 350 430 26 Thikness ≤ 0,7 and > 0,5 – A80% min has to be reduced by 2%.– Thikness ≥ 2 r as to be reduced by 0,2 – For longitudinal test : Re min and max -20Mpa , Rm min and max -10Mpa , A80% +1%
HC300LA 300 380 380 480 23
HC340LA 340 420 410 510 21
HC380LA 380 480 440 560 19
HC420LA 420 520 470 590 17
Bake Hardening steel – Trasversal test
EN 10268
HC180B 180 230 300 360 34 Thikness ≤ 0,7 e > 0,5 – A80% min has to be reduced by 2%.— Thikness ≥ 2 r as to be reducede by 0,2 –
HC220B 220 270 320 400 32
HC260B 260 320 360 440 29
HC300B 300 360 400 480 26
Interstitial Free steel – Trasversal steel
EN 10268
HC180Y 180 230 340 400 36 Thikness ≤ 0,7 e > 0,5 – A80% min has to be reduced 2%.P– Thikness ≥ 2 r has to be reduced by 0,2 –
HC220Y 220 270 350 420 34
HC260Y 260 320 380 440 32

Hot dipped galanized

Qual UNI / Norma Re Min Re Max Rm Min Rm Max A80% Note
Drawing and bending steel, Hot dipped Galvanized. Trasversal test 
EN 10346  
DX51D+Z – – 270 500 22 A per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4%
DX52D+Z 140 300 270 420 26
DX53D+Z 140 260 270 380 30
DX54D+Z 120 220 260 350 36
As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4% – As per thikness < 1,5 il value of r must be reduced by 0,2
DX56D+Z 120 180 260 350 39
DX57D+Z 120 170 260 350 41 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4%
Structural steel, Hot dipped galvanized. Longitudinal test 
EN 10346  
S220GD+Z 220 – 300 – 20 Pas per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4%
S250GD+Z 250 – 330 – 19
S280GD+Z 280 – 360 – 18
S320GD+Z 320 – 390 – 17
S350GD+Z 350 – 420 – 16
S550GD+Z 550 – 560 – –
InterstitialFree Steel, Hot dipped galvanized. Trasversal test 
EN 10346  
HX160YD+Z 160 220 300 360 37 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced 4% – As per thikness > 1,5 value of r must be reduced by 0,2
HX180YD+Z 180 240 330 390 34
HX220YD+Z 220 280 340 420 32
HX260YD+Z 260 320 380 440 30
HX300YD+Z 300 360 390 470 27
Bake Hardening Steel, Hot Dipped Galvanized. Trasversal test 
EN 10346  
HX220BD+Z 220 280 320 400 32 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4% – As per thikness > 1,5 value of r must be reduced by 0,2
HX260BD+Z 260 320 360 440 28
HX260LAD+Z 260 330 350 430 26
HX300BD+Z 300 360 400 480 26
HX340BD+Z 340 400 440 520 24
High resistenzial Micro-Alloy Steel , Hot dipped galvanized. Trasversal test 
EN 10346  
HX260LAD+Z 260 330 350 430 26 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4% – As per thikness > 1,5 value of r must be reduced by 0,2
HX300LAD+Z 300 380 380 480 23
HX340LAD+Z 340 420 410 510 21
HX380LAD+Z 380 480 440 560 19
HX420LAD+Z 420 520 470 590 17
HX460LAD+Z 460 560 500 640 15
HX500LAD+Z 500 620 530 690 13
Dual Phase(DP) Steel, Hot dipped galavnized. Trasversal test 
EN 10346  
HCT450X+Z 260 340 450 – 27 As per thikness ≤ 0,7 and > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4%
HCT500X+Z 300 380 500 – 23
HCT600X+Z 340 420 600 – 20
HDT580X+Z 330 460 580 – 19  
HCT780X+Z 450 560 780 – 14 As per thikness ≤ 0,7 and > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4%
HCT980X+Z 600 750 980 – 10
Coating Masses (gsup /mq grams) avaible
100 – 140 – 200 – 225 – 275 – 350 – 450 – 600
Surface finishes avaible N oppure M
Superficial Quality avaible  
As per finish M: A – B – C
As per finish N: A
Obtainable surface avaible C – O – CO – P – PO – S – U

Eectrogalvanized

Qual UNI / Norma Re Min Re Max Rm Min Rm Max A80% NOTE
Deep drawing and cold bending Steel , Electrogalvanized. On Cold Rolled Steel base. Trasversal test 
EN 10152  
DC01+ZE 140 280 270 410 28 Nota1 As per thikness ≤ 0,7 e > 0,5 – Re max + 20 Mpa and A80% min – 2%. Note2 As per thikness ≤ 0,5 Re max + 40 Mpa and A80% min – 4%. Note3: r and n shall be applied for thikness ≥ 0,5. Note4: As per thikness > 2 r – 0,2
DC03+ZE 140 240 270 370 34
DC04+ZE 140 220 270 350 37
DC05+ZE 140 200 270 330 39
DC06+ZE 130 180 270 350 41
DC07+ZE 110 160 250 310 43
Avaible coating (Micron each side ) 1 side
1,5/0 – 5,0/0 – 7,5/0 – 10/0
      2 sides
2,5/2,5 – 5,0/5,0 – 7,5/7,5 – 10/10
Also avaible with electrogalvanized coating:
 Micro Alloy steel (HC) EN 10268 . Pls refer to sector related to Cold rolled Steel
Acciai a basso tenore di carbonio per stampaggio a freddo (DD), high yeld limit for cold forming (S) EN 10149, Structural steel (S) EN 10025 , for the characteristics of wich we refer ti the hot rolled sector

Other hot dipped galvanized

Qual UNI / Norma Re Min Re Max Rm Min Rm Max A80% Note
Aluminated Deep Drawing and bending Steel Trasversal test
EN 10346
DX51D+AS – – 270 500 22 Note1 A per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by4%
DX52D+AS 140 300 270 420 26
DX53D+AS 140 260 270 380 30
DX54D+AS 120 220 260 350 34 Note1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced byl 4% – note2 as per thikness < 1,5 value of r must be reduced by 0,2 – note3 as per thikness ≤ 0,7 r must be reduced by 0,2 and n must be reduced by 0,01
DX55D+AS 140 240 270 370 30 Note1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per thikness ≤ 0,5 -A80% min must be reduced by 4%
DX56D+AS 120 180 260 350 39 Note1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per value ≤ 0,5 -A80% min must be reduced by 4% – note2 as per thikness < 1,5 il value of r must be reduced by 0,2 – note3 as per thikness ≤ 0,7 r must be reduced by 0,2 and n must be reduced by 0,01
DX57D+AS 120 170 260 350 41
Aluminated InterstitionalFree Steel. Trasversal test
EN 10346
HX160YD+AS 160 220 300 360 35 Note 1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per value ≤ 0,5 -A80% min must be reduced by 4% – note2 as per thikness > 1,5 vale of r must be reduced by 0,2
HX180YD+AS 180 240 330 390 32
HX220YD+AS 220 280 340 420 30
HX260YD+AS 260 320 380 440 28
HX300YD+AS 300 360 390 470 25
Aluminated High resistential Micro-Alloy Steel. Trasversal test
EN 10346
HX260LAD+AS 260 330 350 430 24 Nota1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per value ≤ 0,5 -A80% min must be reduced by 4% – note2 as per thikness > 1,5 value of r must be reduced by 0,2
HX300LAD+AS 300 380 380 480 21
HX340LAD+AS 340 420 410 510 19
HX380LAD+AS 380 480 440 560 17
HX420LAD+AS 420 520 470 590 15
HX460LAD+AS 460 560 500 640 13
HX500LAD+AS 500 620 530 690 11
Aluminated Structural Steel . Longitudinal test
EN 10346
S250GD+AS 250 – 330 – 19 Note1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per value ≤ 0,5 -A80% min must be reduced by 4%
S280GD+AS 280 – 360 – 18
S320GD+AS 320 – 390 – 17
S350GD+AS 350 – 420 – 16
Coating masses (grams on each surf/mq ) avaible 60 – 80 – 100 -120 – 150
Superficial Quality avaible A – B – C
Superficial Treatments avaible C / O / CO / P / PO / S / U
Aluzinc Deep Drawing and bending Steel Trasversal test
EN 10346
DX51D+AZ – – 270 500 22 Note1 A per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by4%
DX52D+AZ 140 300 270 420 26
DX53D+AZ 140 260 270 380 30
DX54D+AZ 120 220 260 350 36
Aluzinc InterstitionalFree Steel. Trasversal test
EN 10346
HX160YD+AZ 160 220 300 360 35 Note 1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per value ≤ 0,5 -A80% min must be reduced by 4% – note2 as per thikness > 1,5 vale of r must be reduced by 0,2
HX180YD+AZ 180 240 330 390 32
HX220YD+AZ 220 280 340 420 30
HX260YD+AZ 260 320 380 440 28
HX300YD+AZ 300 360 390 470 25
Aluzinc High resistential Micro-Alloy Steel. Trasversal test
EN 10346
HX260LAD+AZ 260 330 350 430 24 Note 1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per value ≤ 0,5 -A80% min must be reduced by 4% – note2 as per thikness > 1,5 vale of r must be reduced by 0,2
HX300LAD+AZ 300 380 380 480 21
HX340LAD+AZ 340 420 410 510 19
HX380LAD+AZ 380 480 440 560 17
HX420LAD+AZ 420 520 470 590 15
HX460LAD+AZ 460 560 500 640 13
HX500LAD+AZ 500 620 530 690 11
Aluzinc Structural Steel . Longitudinal test
EN 10346
S220GD+AZ 220 – 300 – 20 Note1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per value ≤ 0,5 -A80% min must be reduced by 4%
S250GD+AZ 250 – 330 – 19
S280GD+AZ 280 – 360 – 18
S320GD+AZ 320 – 390 – 17
S350GD+AZ 350 – 420 – 16
S550GD+AZ 550 – 560 – –
Coating masses (grams on each surf/mq ) avaible 100 – 150 -185
Superficial Quality avaible A – B – C
Superficial Treatments avaible C / O / CO / P / PO / S / U
ZincAluminium Deep Drawing and bending Steel Trasversal test
EN 10346
DX51D+ZA – – 270 500 22 Note1 As per thikness≤ 0,7 and > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4%
DX52D+ZA 140 300 270 420 26
DX53D+ZA 140 260 270 380 30
DX54D+ZA 120 220 260 350 36 Note1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4% – note2 as per thikness < 1,5 value of r must bne reduced by 0,2
DX56D+ZA 120 180 260 350 39
DX57D+ZA 120 170 260 350 41 Note1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4%
Zinc Aluminium DualPhase Steel. Trasversal test
EN 10346
HCT450X+ZA 260 340 450 – 27 Note1 As per thikness≤ 0,7 and > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4%
HCT500X+ZA 300 380 500 – 23
HCT600X+ZA 340 420 600 – 20
HCT780X+ZA 450 560 780 – 14
HCT980X+ZA 600 750 980 – 10
HDT580X+ZA (Base LaC) 330 460 580 – 19
Zinc Aluminium InterstitionalFree Steel. Trasversal test
EN 10346
HX160YD+ZA 160 220 300 360 37 Note1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4% – note2 as per thikness > 1,5 il value of r must be reduced by 0,2
HX180YD+ZA 180 240 330 390 34
HX220YD+ZA 220 280 340 420 32
HX300YD+ZA 300 360 390 470 27
Zinc Aluminium High resistential Micro-Alloy Steel. Trasversal test
EN 10346
HX260LAD+ZA 260 330 350 430 26 Note1 Asper thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per thikness ≤ 0,5 -A80% min must be reduced by 4% – note2 as per thikness > 1,5 value of r must be reduced by 0,2
HX300LAD+ZA 300 380 380 480 23
HX340LAD+ZA 340 420 410 510 21
HX380LAD+ZA 380 480 440 560 19
HX420LAD+ZA 420 520 470 590 17
HX460LAD+ZA 460 560 500 640 15
HX500LAD+ZA 500 620 530 690 13
Zinc AluminiumStructural Steel . Longitudinal test
EN 10346
S220GD+ZA 220 – 300 – 20 Note1 As per thikness ≤ 0,7 and > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4%
S250GD+ZA 250 – 330 – 19
S280GD+ZA 280 – 360 – 18
S320GD+ZA 320 – 390 – 17
S350GD+ZA 350 – 420 – 16
S550GD+ZA 550 – 560 – –
Coating masses (grams on each surf/mq ) avaible 95 -130 – 185 – 200 – 255 – 300
Superficial Quality avaible A – B – C
Superficial Treatments avaible C / O / CO / P / PO / S / U
Galvanealled Deep Drawing and bending Steel Trasversal test
EN 10346
DX51D+ZF – – 270 500 22 Note1 As per thikness≤ 0,7 and > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4%
DX52D+ZF 140 300 270 420 26
DX53D+ZF 140 260 270 380 30
DX54D+ZF 120 220 260 350 34 Note1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4% – note2 as per thikness < 1,5 value of r must bne reduced by 0,2
DX56D+ZF 120 180 260 350 37 Note1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4%
DX57D+ZF 120 170 260 350 39
Galvanealled DualPhase Steel. Trasversal test
EN 10346
HCT450X+ZF 260 340 450 – 25 Note1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4% – note2 as per thikness > 1,5 il value of r must be reduced by 0,2
HCT500X+ZF 300 380 500 – 21
HCT600X+ZF 340 420 600 – 18
HCT780X+ZF 450 560 780 – 12
HCT980X+ZF 600 750 980 – 8
HDT580X+ZF (Su base LaC) 330 460 580 – 19
Galvanealled InterstitionalFree Steel. Trasversal test
EN 10346
HX160YD+ZF 160 220 300 360 35 Note1 As per thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4% – note2 as per thikness > 1,5 il value of r must be reduced by 0,2
HX180YD+ZF 180 240 330 390 32
HX220YD+ZF 220 280 340 420 30
HX260YD+ZF 260 320 380 440 28
HX300YD+ZF 300 360 390 470 25
Galvanealled High resistential Micro-Alloy Steel. Trasversal test
EN 10346
HX260LAD+ZF 260 330 350 430 24 Note1 Asper thikness ≤ 0,7 e > 0,5 – A80% min must be reduced by 2%, as per thikness ≤ 0,5 -A80% min must be reduced by 4% – note2 as per thikness > 1,5 value of r must be reduced by 0,2
HX300LAD+ZF 300 380 380 480 21
HX340LAD+ZF 340 420 410 510 19
HX380LAD+ZF 380 480 440 560 17
HX420LAD+ZF 420 520 470 590 15
HX460LAD+ZF 460 560 500 640 13
HX500LAD+ZF 500 620 530 690 11
Galvanealled Structural Steel . Longitudinal test
EN 10346
S220GD+ZF 220 – 300 – 20 Note1 As per thikness ≤ 0,7 and > 0,5 – A80% min must be reduced by 2%, as per values ≤ 0,5 -A80% min must be reduced by 4%
S250GD+ZF 250 – 330 – 19
S280GD+ZF 280 – 360 – 18
S320GD+ZF 320 – 390 – 17
S350GD+ZF 350 – 420 – 16
S550GD+ZF 550 – 560 – –
Coating masses (grams on each surf/mq ) avaible 100 – 120
Superficial Quality avaible A – B – C
Superficial Treatments avaible C / O / CO / P / PO / S / U

Dimensional tolarances

DIMENSIONAL TOLERANCES HOT ROLLED
STANDARD THIKNESS TOLERANCES EN 10051
Nominal thikness 600 ≤1200″}”>>600 ≤1200 1200≤1500″}”>>1200≤1500 1500≤1800″}”>>1500≤1800 1800″}”>>1800
≤ 2,0 ± 0,17 ± 0,19 ± 0,21 –
2,00 ≤ 2,50″}”>> 2,00 ≤ 2,50 ± 0,18 ± 0,21 ± 0,23 ± 0.25
2,50 ≤ 3,00″}”>> 2,50 ≤ 3,00 ± 0,20 ± 0,22 ± 0,24 ± 0,26
3,00 ≤ 4,00″}”>> 3,00 ≤ 4,00 ± 0,22 ± 0,24 ± 0,26 ± 0,27
4,00 ≤ 5,00″}”>> 4,00 ≤ 5,00 ± 0,24 ± 0,26 ± 0,28 ± 0,29
5,00 ≤ 6,00″}”>> 5,00 ≤ 6,00 ± 0,26 ± 0,28 ± 0,29 ± 0.31
6,00 ≤ 8,00″}”>> 6,00 ≤ 8,00 ± 0,29 ± 0,30 ± 0,31 ± 0,35
8,00 ≤ 10,00″}”>> 8,00 ≤ 10,00 ± 0,32 ± 0,33 ± 0,34 ± 0,40
10,00 ≤ 12,50″}”>>10,00 ≤ 12,50 ± 0,35 ± 0,36 ± 0,37 ± 0,45
12,50 ≤ 15,00″}”>> 12,50 ≤ 15,00 ± 0,37 ± 0,38 ± 0,40 ± 0,46
15,00 ≤ 25,00″}”>> 15,00 ≤ 25,00 ± 0,40 ± 0,42 ± 0,45 ± 0,50
NOTA:
As for S420MC – S460MC – S420N, steels thikness tolerance values must be increased by 30%
As for S500MC – S550MC – S600MC – S700MC steels thikness tolerance values must be increased by 40%
WIDTH TOLERANCES EN 10051
Nominal width Rough edges Trimmed edges
Negative Positive Negative Positive
≤ 1200 0 + 20 0 + 3
1200 ≤ 1500″}”>> 1200 ≤ 1500 0 + 20 0 + 5
1500″}”>> 1500 0 + 25 0 + 6
LENGHT TOLERANCES EN 10051
Nominal width Rough edges Trimmed edges
≤ 2000 – 0 + 10 ± 1
2000 ≤ 8000″}”>> 2000 ≤ 8000 – 0 + 0,005 x nominal leght  ± 1% over the lenght
8000″}”>> 8000 – 0 + 40 –
DIMENSIONAL TOLERANCES COLD ROLLED
THIKNESS TOLERANCES EN 10131 260Mpa≤Re<≤Re<340
Nominal thikness Standard Tolerances Special Tolerances
≤ 1200 1200 ≤ 1500″}”>> 1200 ≤ 1500 1500″}”>> 1500 ≤ 1200 1200 ≤ 1500″}”>> 1200 ≤ 1500 1500″}”>> 1500
≥ 0,35 ≤ 0,40 ± 0,04 ± 0,05 ± 0,06 ± 0,025 ± 0,030 ± 0,035
0,40 ≤ 0,60 “}”>> 0,40 ≤ 0,60 ± 0,04 ± 0,05 ± 0,06 ± 0,030 ± 0,035 ± 0,040
0,60 ≤ 0,80″}”>> 0,60 ≤ 0,80 ± 0,05 ± 0,06 ± 0,07 ± 0,035 ± 0,040 ± 0,050
0,80 ≤ 1,00″}”>> 0,80 ≤ 1,00 ± 0,06 ± 0,07 ± 0,08 ± 0,040 ± 0,050 ± 0,060
1,00 ≤ 1,20″}”>> 1,00 ≤ 1,20 ± 0,07 ± 0,08 ± 0,10 ± 0,050 ± 0,060 ± 0,070
1,20 ≤ 1,60″}”>> 1,20 ≤ 1,60 ± 0,09 ± 0,11 ± 0,12 ± 0,060 ± 0,070 ± 0,080
1,60 ≤ 2,00″}”>> 1,60 ≤ 2,00 ± 0,12 ± 0,13 ± 0,14 ± 0,070 ± 0,080 ± 0,100
2,00 ≤ 2,50″}”>> 2,00 ≤ 2,50 ± 0,14 ± 0,15 ± 0,16 ± 0,100 ± 0,110 ± 0,120
2,50 ≤ 3,00″}”>> 2,50 ≤ 3,00 ± 0,17 ± 0,18 ± 0,18 ± 0,120 ± 0,130 ± 0,140
THIKNESS TOLERANCES EN 10131 340Mpa ≤Re>420Mpa
Nominal thikness Standard Tolerances Special Tolerances
≤ 1200 1200 ≤ 1500″}”>> 1200 ≤ 1500 1500″}”>> 1500 ≤ 1200 1200 ≤ 1500″}”>> 1200 ≤ 1500 1500″}”>> 1500
≥ 0,35 ≤ 0,40 ± 0,04 ± 0,05 ± 0,06 ± 0,030 ± 0,035 ± 0,040
0,40 ≤ 0,60 “}”>> 0,40 ≤ 0,60 ± 0,05 ± 0,06 ± 0,07 ± 0,035 ± 0,040 ± 0,050
0,60 ≤ 0,80″}”>> 0,60 ≤ 0,80 ± 0,06 ± 0,07 ± 0,08 ± 0,040 ± 0,050 ± 0,060
0,80 ≤ 1,00″}”>> 0,80 ≤ 1,00 ± 0,07 ± 0,08 ± 0,10 ± 0,050 ± 0,060 ± 0,070
1,00 ≤ 1,20″}”>> 1,00 ≤ 1,20 ± 0,09 ± 0,10 ± 0,11 ± 0,060 ± 0,070 ± 0,080
1,20 ≤ 1,60″}”>> 1,20 ≤ 1,60 ± 0,11 ± 0,12 ± 0,14 ± 0,070 ± 0,080 ± 0,100
1,60 ≤ 2,00″}”>> 1,60 ≤ 2,00 ± 0,14 ± 0,15 ± 0,17 ± 0,080 ± 0,100 ± 0,110
2,00 ≤ 2,50″}”>> 2,00 ≤ 2,50 ± 0,16 ± 0,18 ± 0,19 ± 0,110 ± 0,120 ± 0,130
2,50 ≤ 3,00″}”>> 2,50 ≤ 3,00 ± 0,20 ± 0,20 ± 0,21 ± 0,130 ± 0,140 ± 0,150
THIKNESS TOLERANCES EN 10131 Re≥420Mpa
Nominal thikness Standard Tolerances Special Tolerances
≤ 1200 1200 ≤ 1500″}”>> 1200 ≤ 1500 1500″}”>> 1500 ≤ 1200 1200 ≤ 1500″}”>> 1200 ≤ 1500 1500″}”>> 1500
≥ 0,35 ≤ 0,40 ± 0,05 ± 0,06 ± 0,07 ± 0,035 ± 0,040 ± 0,050
0,40 ≤ 0,60 “}”>> 0,40 ≤ 0,60 ± 0,05 ± 0,07 ± 0,08 ± 0,040 ± 0,050 ± 0,060
0,60 ≤ 0,80″}”>> 0,60 ≤ 0,80 ± 0,06 ± 0,08 ± 0,10 ± 0,050 ± 0,060 ± 0,070
0,80 ≤ 1,00″}”>> 0,80 ≤ 1,00 ± 0,08 ± 0,10 ± 0,11 ± 0,060 ± 0,070 ± 0,080
1,00 ≤ 1,20″}”>> 1,00 ≤ 1,20 ± 0,10 ± 0,11 ± 0,13 ± 0,070 ± 0,080 ± 0,100
1,20 ≤ 1,60″}”>> 1,20 ≤ 1,60 ± 0,13 ± 0,14 ± 0,16 ± 0,080 ± 0,100 ± 0,110
1,60 ≤ 2,00″}”>> 1,60 ≤ 2,00 ± 0,16 ± 0,17 ± 0,19 ± 0,100 ± 0,110 ± 0,130
2,00 ≤ 2,50″}”>> 2,00 ≤ 2,50 ± 0,19 ± 0,20 ± 0,22 ± 0,130 ± 0,140 ± 0,160
2,50 ≤ 3,00″}”>> 2,50 ≤ 3,00 ± 0,22 ± 0,23 ± 0,24 ± 0,160 ± 0,170 ± 0,180
WIDTH TOLERANCES EN 10131 (COIL)
Nominal width Standard tolerances Restricted tolerances
Negative Positive Negative Positive
≤ 1200 0 + 4 0 +2
1200 ≤ 1500″}”>> 1200 ≤ 1500 0 + 6 0 +2
1500″}”>> 1500 0 + 7 0 +3
WIDTH TOLERANCES EN 10131 (STRIPES/BANDED)
Tolerances class Nominal thikness Nominal width (negative tolerances always = 0)
<125 ≥125<250 ≥250<400 ≥400<600
Standard
 < 0,6 + 0,4 + 0,5 + 0,7 + 1
≥ 0,6 < 1,0 + 0,5 + 0,6 + 0,9 + 1,2
≥ 1,0 < 1,2 + 0,6 + 0,8 + 1,1 + 1,4
≥ 2,0 < 3,0 + 0,7 + 1 + 1,3 + 1,6
Restricted
 < 0,6 + 0,2 + 0,2 + 0,3 + 0,5
≥ 0,6 < 1,0 + 0,2 + 0,3 + 0,4 + 0,6
≥ 1,0 < 1,2 + 0,3 + 0,4 + 0,5 + 0,7
≥ 2,0 < 3,0 + 0,4 + 0,5 + 0,6 + 0,8
LENGHT TOLERANCES EN 10131
Nominal lenght Standard tolerances Restricted tolerances
negative positive negative positive
≤ 2000 0 6 0 3
2000″}”>> 2000 0  0,3% over lenght 0 0,15% over lenght
DIMENSIONAL TOLERANCES HOT DIPPED GALVANIZED
THIKNESS TOLERANCES EN 10143
GENERAL USE STEEL
Nominal thikness Standard tolerances Restricted tolerances
≤ 1200 1200 ≤ 1500″}”>> 1200 ≤ 1500 1500″}”>> 1500 ≤ 1200 1200 ≤ 1500″}”>> 1200 ≤ 1500 1500″}”>> 1500
≤ 0,40 ± 0,05 ± 0,06 – ± 0,03 ± 0,04 –
0,40 ≤ 0,60 “}”>> 0,40 ≤ 0,60 ± 0,06 ± 0,07 ± 0,08 ± 0,04 ± 0,05 ± 0,06
0,60 ≤ 0,80″}”>> 0,60 ≤ 0,80 ± 0,07 ± 0,08 ± 0,09 ± 0,05 ± 0,06 ± 0,06
0,80 ≤ 1,00″}”>> 0,80 ≤ 1,00 ± 0,08 ± 0,09 ± 0,10 ± 0,06 ± 0,07 ± 0,07
1,00 ≤ 1,20″}”>> 1,00 ≤ 1,20 ± 0,09 ± 0,10 ± 0,11 ± 0,07 ± 0,08 ± 0,08
1,20 ≤ 1,60″}”>> 1,20 ≤ 1,60 ± 0,11 ± 0,12 ± 0,12 ± 0,08 ± 0,09 ± 0,09
1,60 ≤ 2,00″}”>> 1,60 ≤ 2,00 ± 0,13 ± 0,14 ± 0,14 ± 0,09 ± 0,10 ± 0,10
2,00 ≤ 2,50″}”>> 2,00 ≤ 2,50 ± 0,15 ± 0,16 ± 0,16 ± 0,11 ± 0,12 ± 0,12
2,50 ≤ 3,00″}”>> 2,50 ≤ 3,00 ± 0,17 ± 0,18 ± 0,18 ± 0,12 ± 0,13 ± 0,13
THIKNESS TOLERANCES EN 10143
STRUCTURAL STEEL Re≥280 (Nmm2)
Nominal thikness Standard tolerances Restricted tolerances
≤ 1200 1200 ≤ 1500″}”>> 1200 ≤ 1500 1500″}”>> 1500 ≤ 1200 1200 ≤ 1500″}”>> 1200 ≤ 1500 1500″}”>> 1500
≤ 0,40 ± 0,06 ± 0,07 – ± 0,04 ± 0,05 –
0,40 ≤ 0,60 “}”>> 0,40 ≤ 0,60 ± 0,07 ± 0,08 ± 0,09 ± 0,05 ± 0,06 ± 0,07
0,60 ≤ 0,80″}”>> 0,60 ≤ 0,80 ± 0,08 ± 0,09 ± 0,11 ± 0,06 ± 0,07 ± 0,07
0,80 ≤ 1,00″}”>> 0,80 ≤ 1,00 ± 0,09 ± 0,11 ± 0,12 ± 0,07 ± 0,08 ± 0,08
1,00 ≤ 1,20″}”>> 1,00 ≤ 1,20 ± 0,11 ± 0,12 ± 0,13 ± 0,08 ± 0,09 ± 0,09
1,20 ≤ 1,60″}”>> 1,20 ≤ 1,60 ± 0,13 ± 0,14 ± 0,14 ± 0,09 ± 0,11 ± 0,11
1,60 ≤ 2,00″}”>> 1,60 ≤ 2,00 ± 0,15 ± 0,15 ± 0,17 ± 0,11 ± 0,12 ± 0,12
2,00 ≤ 2,50″}”>> 2,00 ≤ 2,50 ± 0,18 ± 0,18 ± 0,19 ± 0,13 ± 0,14 ± 0,14
2,50 ≤ 3,00″}”>> 2,50 ≤ 3,00 ± 0,20 ± 0,20 ± 0,21 ± 0,14 ± 0,15 ± 0,15
WIDTH TOLERANCES EN 10143 (COIL)
Nominal width Standard tolerances Restricted tolerances
Negative Positive Negative Positive
≤ 1200 0 + 5 0 +2
1200 ≤ 1500″}”>> 1200 ≤ 1500 0 + 6 0 +2
1500″}”>> 1500 0 + 7 0 +3
WIDTH TOLERANCES EN 10143 (STRIPES/BANDED)
Tolerances class Nominal thikness Nominal width (negative tolerances always = 0)
<125 ≥125<250 ≥250<400 ≥400<600
Standard < 0,6 + 0,4 + 0,5 + 0,7 + 1
≥ 0,6 < 1,0 + 0,5 + 0,6 + 0,9 + 1,2
≥ 1,0 < 1,2 + 0,6 + 0,8 + 1,1 + 1,4
≥ 2,0 < 3,0 + 0,7 + 1 + 1,3 + 1,6
Restricted < 0,6 + 0,2 + 0,2 + 0,3 + 0,5
≥ 0,6 < 1,0 + 0,2 + 0,3 + 0,4 + 0,6
≥ 1,0 < 1,2 + 0,3 + 0,4 + 0,5 + 0,7
≥ 2,0 < 3,0 + 0,4 + 0,5 + 0,6 + 0,8
LENGHT TOLERANCES EN 10143
Nominal lenght Standard tolerances Restricted tolerances
negative positive negative positive
≤ 2000 0 6 0 3
2000″}”>> 2000 0 0,3% over lenght 0 0,15% over lenght
8000″}”>> 8000 to be agreeded